Short curing time bulk fill composite systems: volumetric shrinkage, degree of conversion and Vickers hardness.

This study aimed to evaluate volumetric polymerization shrinkage, degree of conversion and Vickers hardness of four bulk-fill resin composites light-activated with their dedicated light curing units (LCUs). Four groups were evaluated, according to the type of composite and curing mode: Tetric EvoCeram Bulk-fill (TEBO) and Tetric EvoFlow Bulk-fill (TEBF) were light-activated with Bluephase Style 20i (20s, in high-mode), while Tetric Powerfill (TEPO) and Tetric Powerflow (TEPF) were light-activated with Bluephase PowerCure (3s). Volumetric polymerization shrinkage test (n = 6) was performed in standardized box-shaped class-I cavities of extracted third molars (4 x 4 x 4 mm). Teeth were scanned before and after resin composite application by micro-computed tomography, and acquired data were evaluated with Amira software. Degree of conversion (n = 5) was evaluated at the top and bottom surfaces of composite cylindric samples (4 mm diameter, 4 mm thickness) using an FT-IR spectrometer (spectra between 1,500 and 1,800 cm-1, 40 scans at a resolution of 4 cm-1). Three Vickers indentations (50 g / 15 s), spaced 500 µm apart, were performed on the top and bottom composite surfaces and averaged. One-way ANOVA was used for data evaluation. TEPF showed the lowest volumetric polymerization shrinkage (p < 0.05), while the other composites were not significantly different within each other (p > 0.05). All materials presented a significant decrease in degree of conversion and Vickers hardness when compared top to bottom surfaces (p < 0.05). Bottom to top surface ratios for degree of conversion ranged from 0.8 (TEBO and TEPO) to 0.9 (TEBF and TEPF), and from 0.4 (TEPO) to 0.7 (TEBF and TEPF) for hardness. In conclusion, resinous materials present a decrease in hardness and degree of conversion from top to bottom even when a higher power is used, while the flowable material TEPF showed the lowest volumetric shrinkage values compared to the other materials.

Automotive Technology Revolutionized Restorative Dentistry Discovery of Alpha-diketone/Amine Catalyst: Part I.

A full account of early research that led to the discovery of the Alpha-diketone and Amine systems by two Imperial Chemical Industries (ICI) researchers. UK Chemists in the mid-sixties marked the beginning in the early development of a composite resin cured with visible light spectrum into a solid mass. Its incorporation into the newly developed Urethane based resin, led to conceiving the idea of developing the first light-activated restorative composite resin, which formed the prototype of modern composite restorative materials. How all that came about, and the ideas that were conceived and pursued in the development of these systems are discussed in detail.

Effect of acidic environment on color and translucency of different indirect restorative materials.

PURPOSE: The aim of the current study was to evaluate the effect of simulated gastric acid on the color and translucency of different indirect restorative materials. MATERIALS AND METHODS: A total of 36 disc-shaped samples were cut by using an isomet saw and divided into four equal groups (n = 9) according to the material type: Group Z: translucent zirconia (Ceramill® Zolid ht.+ preshade, Amann Girrbach, Koblach, Austria); Group E: lithium disilicate (IPS e.max CAD, Ivoclar Vivadent AG, Schaan, Liechtenstein); Group C: resin nanoceramic (Cerasmart, GC, Tokyo, Japan); Group P: polyether ether ketone (PEEK) (Bettin Zirconia Dentale Italy) veneered with indirect high impact polymer composite (HIPC) (breCAM HIPC, Bredent GmbH & Co. KG, Germany). The samples were immersed in simulated gastric acid (HCl, pH 1.2) for 96 hours at 37 °C in an incubator. The color change (ΔE00) and translucency (RTP00) were measured every 9.6 hours (one-year clinical simulation) of immersion in simulated gastric acid. RESULTS: For color change (∆E00) and translucency (RTP00) among the tested materials, there was a highly statistically significant difference (P < 0.001) after every year of follow-up. The color change in both Z and G groups was the lowest after 1 year of acid immersion, followed by that in group H, and the highest change in color was recorded in group P. CONCLUSION: High translucent zirconia is recommended in patients who are concerned about esthetic, especially with acidic oral environment.

Development of ZTA (80% Al2O3/20% ZrO2) pre-sintered blocks for milling in CAD/CAM systems.

The present work aims to develop a production method of pre-sintered zirconia-toughened-alumina (ZTA) composite blocks for machining in a computer-aided design and computer-aided manufacturing (CAD-CAM) system. The ZTA composite comprised of 80% Al2O3 and 20% ZrO2 was synthesized, uniaxially and isostatically pressed to generate machinable CAD-CAM blocks. Fourteen green-body blocks were prepared and pre-sintered at 1000 °C. After cooling and holder gluing, a stereolithography (STL) file was designed and uploaded to manufacture disk-shaped specimens projected to comply with ISO 6872:2015. Seventy specimens were produced through machining of the blocks, samples were sintered at 1600 °C and two-sided polished. Half of the samples were subjected to accelerated autoclave hydrothermal aging (20h at 134 °C and 2.2 bar). Immediate and aged samples were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). Optical and mechanical properties were assessed by reflectance tests and by biaxial flexural strength test, Vickers indentation and fracture toughness, respectively. Samples produced by machining presented high density and smooth surfaces at SEM evaluation with few microstructural defects. XRD evaluation depicted characteristic peaks of alpha alumina and tetragonal zirconia and autoclave aging had no effect on the crystalline spectra of the composite. Optical and mechanical evaluations demonstrated a high masking ability for the composite and a characteristic strength of 464 MPa and Weibull modulus of 17, with no significant alterations after aging. The milled composite exhibited a hardness of 17.61 GPa and fracture toughness of 5.63 MPa m1/2, which remained unaltered after aging. The synthesis of ZTA blocks for CAD-CAM was successful and allowed for the milling of disk-shaped specimens using the grinding method of the CAD-CAM system. ZTA composite properties were unaffected by hydrothermal autoclave aging and present a promising alternative for the manufacture of infrastructures of fixed dental prostheses.

The Impact of Gastric Juice on the Surface Roughness of Surface Sealant-Treated Provisional Restorations.

BACKGROUND AND AIM: Gastroesophageal reflux disease causes gastric acid to enter the oral cavity, leading to mucosal changes and deterioration of dental hard tissues and materials. The purpose of this in vitro study was to evaluate the impact of gastric juice on the surface roughness of two types of acrylics used in provisional restorations. MATERIALS AND METHODS: Acrytemp ® and Temdent acrylic resin discs (10 × 2 mm) totaling 80 were manufactured and divided into eight groups (n = 10). Groups were prepared as follows: Group 1 (Temdent + Universal Polish) (control), Group 2 (Temdent + Universal Polish + Biscover LV), Group 3 (Temdent + Universal Polish + Resin Glaze), Group 4 (Temdent + Universal Polish + Fortify Plus), Group 5 (Acrytemp + Universal Polish) (control), Group 6 (Acrytemp + Universal Polish + Biscover LV), Group 7 (Acrytemp + Universal Polish + Resin Glaze), and Group 8 (Acrytemp + Universal Polish + Fortify Plus). The resin discs were immersed in distilled water for 24 h and in gastric juice (pH = 2) for additional 24 h. The initial and final roughness values of samples were measured and analyzed with non-parametric statistics including Mann-Whitney U-test for pairwise comparison, Kruskall Wallis test for comparing more than two groups, and Wilcoxon signed rank test for within-group comparison (P < 0.05). RESULTS: Surface roughness did not differ significantly between control groups. It notably increased for all samples with surface sealants, both initially and after gastric juice immersion (P < 0.05). CONCLUSION: Surface sealants noticeably increased the roughness of two types of acrylic resins. After immersing in gastric juice, Group 4 (Temdent + Universal Polish + Fortify Plus) showed the highest roughness, while the untreated control groups remained the smoothest.

The effect of various inhaled asthma medications on the color stability of paediatric dental restorative materials.

BACKGROUND: The purpose of the study is to analyse the effects of different inhaled asthma medications (IAMs) on the color change of dental restorative materials (DRMs). METHODS: In total, 192 samples were taken from six different DRMs: [Filtek Z550 (nanohybrid composite), Fusio Liquid Dentin (Self-adhering flowable composite), Filtek Ultimate (nanofilled flowable composite), Dyract XP (compomer), Fuji II LC (resin-modified glass ionomer), Fuji IX Fast (self-cured-packable glass ionomer), (n = 32)]. After the initial color values (CIELab) of DRMs were measured by using a spectrophotometer, each sample was exposed to the same IAMs via nebulizer according to the four different inhaled therapies and measurements were repeated on the 7th & 21st days. RESULTS: In all IAM groups, DRM with the least amount of ΔE was nanohybrid composite, while the highest ΔE was found in Fuji II LC. Among all experimental groups, only Fuji II LC which was administered the combined medication, exceeded the clinically unacceptable threshold (ΔE = 3.3) on 7th & 21st days. CONCLUSIONS: Consequently, important factors affecting the susceptibility to color stability are the type of IAMs, the administration time-dosage, and the type of DRMs.

Niobium oxyhydroxide as a bioactive agent and reinforcement to a high-viscosity bulk-fill resin composite.

OBJECTIVE: The present in vitro study incorporated niobium oxyhydroxide fillers into an experimental high-viscosity bulk-fill resin composite to improve its mechanical performance and provide it a bioactive potential. METHODOLOGY: Scanning electron microscopy synthesized and characterized 0.5% niobium oxyhydroxide fillers, demonstrating a homogeneous morphology that represented a reinforcement for the feature. Fillers were weighed, gradually added to the experimental resin composite, and homogenized for one minute, forming three groups: BF (experimental high-viscosity bulk-fill resin composite; control), BF0.5 (experimental high-viscosity bulk-fill resin composite modified with 0.5% niobium oxyhydroxide fillers), and BFC (commercial bulk-fill resin composite Beautifil Bulk U, Shofu; positive control). In total, 10 specimens/groups (8 × 2 × 2 mm) underwent flexural strength (FS) tests in a universal testing machine (Instron) (500N). Resin composites were also assessed for Knoop hardness (KH), depth of cure (DoC), degree of conversion (DC), elastic modulus (E), and degree of color change (ΔE). The bioactive potential of the developed resin composite was evaluated after immersing the specimens into a simulated body fluid in vitro solution and assessing them using a Fourier-transformed infrared spectroscope with an attenuated total reflectance accessory. One-way ANOVA, followed by the Tukey's test (p<0.05), determined FS, DC, KH, and ΔE. For DoC, ANOVA was performed, which demonstrated no significant difference between groups (p<0.05). CONCLUSIONS: The high-viscosity bulk-fill resin composite with 0.5% niobium oxyhydroxide fillers showed promising outcomes as reinforcement agents and performed well for bioactive potential, although less predictable than the commercial resin composite with Giomer technology.

Effects of multiple firings on the translucency, crystalline phase, and mechanical strength of highly translucent zirconia.

This study aimed to clarify the effects of multiple firings on the translucency, crystal structure, and mechanical strength of highly translucent zirconia. Four types of highly translucent zirconia (LAVA Esthetic, LAVA Plus, KATANA Zirconia STML, and KATANA Zirconia HTML) were fired three times at three different temperatures, and the translucency, crystal structure, and flexural strength were evaluated before and after firing. The translucency was statistically compared using repeated-measures analysis of variance; the zirconia phase composition was assessed using X-ray diffraction followed by Rietveld analysis; and the biaxial flexural strength was assessed using Weibull analysis. The translucency of LAVA Esthetic and KATANA Zirconia HTML decreased significantly after firing, and the crystal composition of LAVA Plus and KATANA Zirconia HTML changed after multiple firings, whereas multiple firings did not affect the biaxial flexural strength of any samples. Thus, multiple firings may affect the optical properties of highly translucent zirconia.

Two-year evaluation of a nano-hybrid and a bulk-fill resin composite: a randomized, double-blind split-mouth clinical study.

OBJECTIVES: The aim of this study was to compare the 2-year clinical performance of a bulk-fill composite resin and a nano-hybrid-filled composite resin in 6-12-year-old children in a split-mouth design. MATERIALS AND METHODS: This randomized, split-mouth, and double-blind study was conducted on 89 patients aged 6-12 years with caries on bilateral mandibular first molars. In a split-mouth design, restorations of mandibular permanent molars were completed with nano-hybrid organically modified ceramic (ORMOCER)-based bulk-fill composite resin Admira Fusion x-tra (Voco GmbH, Cuxhaven, Germany) and nano-hybrid composite Grandio (Voco, Cuxhaven, Germany). Futurabond U single dose (Voco, Cuxhaven, Germany) was used with selective enamel etching. The clinical success of the restorations was evaluated using USPHS and FDI criteria at 6, 12, and 24-month follow-up controls. RESULTS: In the 2-year follow-up, all restorations were clinically acceptable. Grandio was significantly worse than Admira Fusion x-tra in terms of surface luster and superficial change (p < 0.05). Surface staining and color match scores increased in Admira Fusion x-tra compared with Grandio significantly (p < 0.05). CONCLUSIONS: Although both materials showed acceptable clinical performance over 2 years, a significant difference was observed between the surface luster, surface staining, marginal adaptation, and staining of the nano-hybrid composite placed with the incremental technique and the bulk-fill ORMOCER-based composite resin. CLINICAL RELEVANCE: As an alternative to nano-hybrid composite resins, using bulk-fill restorative materials, which can be indicated in the proper case, may contribute to shortening treatment procedures and increasing patient and physician comfort, leading to clinical success.

Influence of printing orientation on mechanical properties of aged 3D-printed restorative resins.

OBJECTIVE: To evaluate the influence of printing orientation on flexural strength (σf) and elastic modulus (E) of different 3D printing dental restorative resins. METHODS: Bar-shaped specimens (n = 20) were fabricated from two SLA-printed resins (FT- Formlabs Temporary, and FP- Formlabs Permanent) and two DLP-printed resins (DFT- Detax Freeprint Temp, and GCT- GC Temporary) using two building orientations (0º and 90º). The 3D-printed structures were aged (14 d) before submitted to three-point bending in 37ºC distilled water at a crosshead speed of 1.0 ± 0.3 mm/min until fracture to calculate the σf and the E values. The fractured surfaces were evaluated using stereomicroscopy and scanning electron microscopy (SEM) following fractography principles. Data were statistically analyzed using two-way ANOVA and Tukey post-hoc (α = 0.001). RESULTS: FP and FT showed significantly higher E values than DFT and GCT, irrespectively of printing orientation (p < 0.001). There was no statistical difference between the building orientations (0º and 90º) for the mean σf and E values for the resin materials evaluated. Fractographic characteristics were similar for the surface fracture from all the materials evaluated, showing typical brittle fracture behavior. SIGNIFICANCE: Printing orientation did not influence of flexural strength and elastic modulus values for the 3D-printed resin structures evaluated. Surface topography was mostly governed by the 3D printer type.

Biomechanical Behavior of a 3D-Printed Denture Base Material.

PURPOSE: To evaluate relevant material properties (flexural strength [σf], elastic modulus [E], water sorption [Wsp] and solubility [Wsl], and biocompatibility) of an additive manufacturing (AM) polymer vs a heat-curing acrylic resin (AR; control) for the manufacture of complete dentures, testing the hypothesis that fabrications from both materials would present acceptable material properties for clinical use. MATERIALS AND METHODS: The σf, E, Wsp, and Wsl were evaluated according to the ISO 20795-1:2013 standard, and the biocompatibility was evaluated using MTT and SRB assays. Disk-shaped specimens were fabricated and used for Wsp (n = 5), Wsl (n = 5), and biocompatibility (n = 3) testing. For assessment of σf and E, bar-shaped specimens (n = 30) were fabricated and stored in 37°C distilled water for 48 hours or 6 months before flexural testing in a universal testing machine with a constant displacement rate (5 ± 1 mm/minute). Data from σf, E, Wsp, Wsl, and biocompatibility tests were statistically analyzed using Student t test (α = .05). Weibull analysis was also used for σf and E data. RESULTS: Significant differences between the two materials were found for the evaluated material properties. Water storage for 6 months did not affect the flexural strength of the AM polymer, but this material showed inadequate σf and Wsl values. CONCLUSIONS: Despite adequate biocompatibility and strength stability after 6 months of water storage, the AM polymer recommended for complete dentures needs further development to improve the material properties evaluated in this study.

Effect of Food-Simulating Liquids on the Mechanical Properties of 3D-Printed Provisional Restoration Materials.

PURPOSE: To evaluate the effect of food-simulating liquids (FSLs) on the mechanical properties of provisional restoration materials fabricated by 3D printing, milling, and traditional fabricating methods. MATERIALS AND METHODS: The bar specimens were fabricated with traditional, milling, and 3D-printing methods according to ISO 10477 specifications. Each group of specimens was randomly subdivided into four groups to be immersed in various FSLs: distilled water (control group), n-heptane, 50% ethyl alcohol, and 0.02 mol/L citric acid for 7 days at room temperature (n = 19 per group). The Knoop hardness (KHN) was evaluated, and the specimens were subjected to a three-point bending (3PB) test to evaluate flexural strength (FS) and flexural modulus (FM). One-way ANOVA and Tukey tests were used to analyze the data. RESULTS: Fabrication methods had a significant effect on the mechanical properties of the materials being tested. FSLs had no effect on the FS and FM of materials being tested. The 50% ethyl alcohol solution significantly decreased the hardness of traditional group specimens, and the n-heptane and 50% ethyl alcohol solutions increased the hardness of the 3D-printed specimens significantly (P ≤ .05). Scanning electron microscopy (SEM) revealed that while traditional and milling group specimens showed a ductile fracture type, 3D-printed specimens showed a brittle fracture type. CONCLUSIONS: Production methods affected the mechanical properties of provisional restoration materials. Immersion in 50% ethyl alcohol solution decreased the KHN of the traditional specimens. FSLs had no negative effect on the mechanical properties of the milled and 3D-printed specimens.

Effect of Hydrothermal Aging on the Flexural Strength and Microhardness of Materials Used for Additive or Subtractive Manufacturing of Definitive Restorations.

PURPOSE: To evaluate the flexural strength (FS) and microhardness of various CAD/CAM restorative materials intended for definitive use. The effect of hydrothermal aging on the mechanical properties of these materials was also investigated. MATERIALS AND METHODS: A total of 210 bar-shaped specimens (17 × 4 × 1.5 mm ± 0.02 mm) were fabricated via either subtractive manufacturing (SM) methods-reinforced composite resin (SM-CR), polymer-infiltrated ceramic network (SM-PICN), fine-structured feldspathic ceramic (SMFC), nanographene-reinforced polymethyl methacrylate (PMMA; SM-GPMMA), PMMAbased resin (SM-PMMA)-or additive manufacturing (AM) methods with urethane acrylate-based resins (AM-UA1 and AM-UA2). Specimens were then divided into two subgroups (nonaged or hydrothermal aging; n = 15). A three-point flexural strength test was performed, and five specimens from the nonaged group were submitted to microhardness testing. Specimens were subjected to 10,000 thermal cycles, and the measurements were repeated. RESULTS: Regardless of aging, SM-CR had the highest FS (P < .001), followed by SM-GPMMA (P ≤ .042). In nonaged groups, AM-UA2 had a lower FS than all other materials except SM-FC (P = 1.000). In hydrothermal aging groups, AM specimens had lower FS values than other materials, except SM-PMMA. With regard to microhardness, there was no significant difference found between any of the tested materials (P ≥ .945) in the nonaged and hydrothermal aging groups. CONCLUSIONS: The effect of hydrothermal aging on FS varied depending on the type of restorative material. Regardless of aging condition, SM-CR showed the highest FS values, whereas SM-FC had the highest microhardness. Hydrothermal aging had no significant influence on the microhardness of the tested materials.

Zirconia dental implants; the relationship between design and clinical outcome: A systematic review.

OBJECTIVE: To evaluate the clinical outcome of different designs of zirconia dental implants. DATA: This systematic review adhered to the PRISMA checklist and followed the PICO framework. The protocol is registered in PROSPERO (CRD42022337228). SOURCES: The search was conducted in March 2023 through four databases (PubMed, Web of Science, Cochrane Library, and Google Scholar) along with a search of references in the related reviews. Three authors reviewed on title, and abstract level and analysed the risk of bias, and all authors reviewed on a full-text level. STUDY SELECTION: Clinical studies excluding case reports for patients treated with different designs of zirconia dental implants were included. From a total of 2728 titles, 71 full-text studies were screened, and 27 studies were included to assess the risk of bias (ROBINS-I tool) and data extraction. After quality assessment, four studies were included, and the remaining 23 excluded studies were narratively described. RESULT: The included prospective studies with moderate risk of bias reported success and survival rates of one-piece implants that ranged between 95 and 98.4 % with no difference between different lengths and diameters. The acid-etched roughened surface showed higher clinical outcomes compared to other surface roughness designs. CONCLUSION: Promising 5-year clinical outcomes were found for one-piece zirconia implants with no difference between different diameters and lengths. Concerning surface roughness, better outcomes were found when using the acid-etched implant surface. However, due to the limited available studies, further high-quality clinical studies comparing zirconia one-piece and two-piece implants with different diameters, lengths, and surface roughness are needed. CLINICAL SIGNIFICANCE: Based on this systematic review, under suitable clinical situations, the one-piece zirconia implants with diameters of 4.0 mm, 4.5 mm, or 5.5 mm and lengths of 8 mm, 10 mm, 12 mm, or 14 mm have similar promising clinical outcomes. Additionally, the acid-etched roughened implant surface may be preferable.

Comparative Assessment of Marginal Micro Leakage of Different Esthetic Restorative Materials Used on Primary Teeth: An In-vitro Study.

AIM: The aim of the current investigation was to evaluate the marginal microleakage of various esthetic restorative materials applied to primary teeth. MATERIALS AND METHODS: A total of 75 noncarious primary molars that were removed for orthodontic intervention and teeth nearing exfoliation were chosen. One millimeter (mm) above the cementoenamel junction, on the buccal surface of the teeth, Class V cavities were prepared. William's graded periodontal probe was used to standardize cavity preparation on all teeth. 3 mm was the cavity's length, 2 mm in width, and 2 mm in depth. The teeth were then divided into three groups (25 samples in each group) according to the type of esthetic restorative material used. Group I: Resin-modified glass ionomer cement, Group II: Ormocer, Group III: Giomer. The samples underwent 500 cycles of thermocycling, with an immersion time of 60 seconds and a well time of 15 seconds, between 5 and 55°C. The samples were submerged in methylene blue dye for 24 hours at room temperature and dried. The samples were then divided into sections and examined with a stereomicroscope. Data was recorded and statistically analyzed. RESULTS: The least marginal microleakage was found in the ormocer group (1.22 ± 0.01) followed by resin-modified glass ionomer cement group (1.31 ± 0.07) and the giomer group (1.78 ± 0.03). There was a highly statistically significant difference found between resin-modified glass ionomer cement group and the ormocer group, resin-modified glass ionomer cement group and giomer group. And no significant difference was found between the ormocer group and the giomer group. CONCLUSION: The present study concluded that there was some amount of microleakage in primary teeth in all restorative materials examined in this in-vitro investigation. However, the marginal sealing ability of ormocer was found highest compared to resin-modified glass ionomer cement and Giomer materials. CLINICAL SIGNIFICANCE: The primary reason dental restorations fail, particularly in Class V cavities, is microleakage since the margins of these restorations are typically found in the dentin or cementum. Assessing microleakage is a crucial step in determining the marginal integrity of restorative materials. Developing methods and resources that reduce the adverse effects caused by the restorative marginal seal failing would benefit from this. How to cite this article: Al Ghwainem A, Alqarni AS. Comparative Assessment of Marginal Micro Leakage of Different Esthetic Restorative Materials Used on Primary Teeth: An In-vitro Study. J Contemp Dent Pract 2024;25(1):58-61.

Effect of thermocycling on the mechanical properties of permanent composite-based CAD-CAM restorative materials produced by additive and subtractive manufacturing techniques.

BACKGROUND: The aim of the study was to determine and compare the biaxial flexural strength (BFS) and Vickers hardness (VHN) of additive and subtractive manufactured permanent composite-based restorative materials, before and after thermal aging. METHODS: A total of 200 specimens were prepared; 100 disc-shaped specimens (diameter 13 × 1.2 mm) for the BFS test and 100 square specimens (14 × 14 × 2 mm) for the VHN test. The specimens were made from various materials: two subtractive composite-based blocks (Cerasmart 270 [CS], Vita Enamic [VE]), two additive composite-based resins used for two different vat polymerization methods (digital light processing [DLP]; Saremco Print Crowntec [SC] and stereolithography [SLA]; Formlabs Permanent Crown Resin [FP]), and one feldspathic glass-matrix ceramic block (Vita Mark II [VM]) as the control group. Specimens of each material were divided into two subgroups: thermal cycled or non-thermal cycled (n = 10). BFS and VHN tests were performed on all groups. Data were analyzed with two-way ANOVA and post hoc Tukey test (α = 0.05). RESULTS: The type of restorative material used for the specimen had a statistically significant influence on both BFS and VHN values. However, thermal cycling did not affect the BFS and VHN values. After thermal cycling, the results of the BFS test were ranked from best to worst as follows: CS, FP, SC, VE, then VM. For the VHN values, the order from best to worst was as follows: VM, VE, CS, FP, then SC. CONCLUSIONS: 3D printed and milled composite groups showed higher BFS than feldspathic ceramics. When the VHN results were examined, it was seen that the 3D resin groups had the lowest VHN values. Furthermore, it was observed that the thermal cycle had no effect on BFS or VHN.

Root coverage with the restoration of non-carious cervical lesions: A systematic review and meta-analysis.

The progression of non-carious cervical lesions (NCCLs) leads to gingival recession (GR), which is restored with restorative materials, using different periodontal plastic surgery procedures. There is no consensus on which technique is superior to others. Therefore, the present systematic review aimed to assess the effectiveness of root coverage (RC) procedures in the restored and unrestored NCCLs in terms of clinical and patient-centered outcomes.We used the Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA) while searching 5 databases in addition to the gray literature. The Medical Subject Headings (MeSH) terms and keywords in the title and abstract fields, as well as in headings, were used to search the existing literature for the relevant publications on the effectiveness of RC procedures with the restoration of NCCLs over the past 3 decades (January 1990-July 2021). After applying the inclusion and exclusion criteria, 13 articles were read in full and critically analyzed. The quality analysis was performed using the Cochrane RevMan software.A total of 222 potentially relevant titles and abstracts were found after the initial electronic and manual search, and after removing duplicates. Applying the inclusion and exclusion criteria yielded 23 publications that were further analyzed for relevance and applicability. Following critical analysis, 13 publications were used for validity assessment and data extraction.In the teeth with NCCLs and GR, the restoration of NCCLs does not affect the percentage RC. However, it significantly decreases dentin hypersensitivity, and the patients' perception of esthetics and satisfaction.

Mechanical properties of ion-releasing restorative materials.

PURPOSE: To evaluate and compare the laboratory compressive strength (CS), flexural strength (FS), and diametral tensile strength (DTS) of Cention Forte and three bulk fill restorative materials. METHODS: A total of 168 specimens were prepared following the manufacturers' instructions and standards for testing CS, FS, and DTS. Mechanical properties of Cention Forte (LC-Cent) were compared to three commercial bulk-fill materials for posterior restorations: Fuji IX Extra (Fuji), Tetric PowerFill (TPF), and Equia Forte HT (Equia). The tests were performed 24 hours after storage in distilled water on a universal testing machine at a crosshead speed of 0.75 mm/minute. Strength values (MPa) were calculated and statistically analyzed by one-way ANOVA and Tukey's post hoc test (P< 0.05). RESULTS: Analysis showed significant differences between tested materials for CS, FS, and DTS (P= 0.0001). LC-Cent showed the highest mean value for FS (112.8 MPa) with a significant difference compared to Fuji and Equia. DTS (49.2 MPa) of LC-Cent was significantly higher than all tested materials. TPF showed the highest mean value (180 MPa) for CS but without significant difference compared to LC-Cent. CLINICAL SIGNIFICANCE: Ion-releasing material Cention Forte, according to obtained results, may serve as a viable alternative for posterior restorations compared to conventional bulk-fill restorative materials.